HI-TEMP REPAIR PUTTY

Product Image

HI-TEMP REPAIR PUTTY


SEALXPERT PS108 HI-TEMP REPAIR PUTTY



HI-TEMP REPAIR PUTTY

FEATURES:

  • Withstands high temperature up to 230 °C (446 °F) (continuous) and 280 °C (536 °F) (intermittent)
  • Nickel alloy-filled two-component epoxy putty
  • Suitable for engine parts repairs
  • Can be drilled, tapped, machined or painted

APPLICATION:

  • Used for repairing abrasion, scratch, and crack etc. on equipment operating at high temperature
  • Applicable to watercrafts, automobiles, machineries in petrochemical, power plant etc.

TECHNICAL DATA:

Product No.ColourMixture Ratio (Weight/Volume)Compressive Strength (psi)Tensile Strength (psi)Shear Strength (psi)Hardness (Shore D)Temperature Range (°C/°F)Pot Life (min)Curing Time (hrs)Coverage Area (cm²)50% Load (hrs)100% Load (hrs)
PS 102Grey9:1 / 4:118,130 (1275)4,931 (347)2,901 (204)80-50 to 160 / (-58 to 320)4024-Aug450824
PS 103Aluminium6:1 / 3.5:114,214 (999)4,351 (306)2,611 (184)80-50 to 160 / (-58 to 320)5024-Dec5031224
PS 104Bronze9:1 / 3:113,779 (969)4,351 (306)2,611 (184)80-50 to 170 / (-58 to 338)4024-Aug165824
PS 105Dark Grey11:1 / 3.75:115,229 (1071)4,931 (347)2,901 (204)80-50 to 160 / (-58 to 320)5024-Dec4651224
PS 106Brown5:1 / 3.5:113,053 (918)4,496 (316)2,611 (184)80-50 to 150 / (-58 to 302)2012-Jun472612
PS 107Dark Grey1.7:1 / 1:113,053 (918)3,626 (255)2,611 (184)80-50 to 120 / (-58 to 248)56-Jan4506-Jan1
PS 108Dark Grey5:1 / 4:112,908 (908)4,351 (306)2,611 (184)80-50 to 280 / (-58 to 536)6012-Jun432612
PS 109Dark Grey2:1 / 2:124,656 (1733)7,977 (56)3,046 (214)90-50 to 160 / (-58 to 320)5024-Dec4501224
PS 110Dark Grey11:1 / 3.75:118,855 (1326)4,061 (286)2,031 (143)87-50 to 160 / (-58 to 320)2116-Aug450816

FIRST STAGE: SURFACE PREPARATION

first 1 - Metal Repair Compounds                        first 2 - Metal Repair Compounds
Clean surface thoroughly with solvent              Grit blast surface area with a course file / sandpaper / coarse wheel /                                                                            abrasive disc pad Clean the surface again with solvent

 

SECOND STAGE: MIXTURE

second 1 - Metal Repair Compounds                             second 2 - Metal Repair Compounds
Mix component A (Resin) and component                Continuously scrape material from the sides and bottom of              B (Hardener) in accordance to the specified ratio     st_st_container until uniform, streak-free consistency is obtained

      

THIRD STAGE: APPLICATION

third 1 - Metal Repair Compounds                             third 2 - Metal Repair Compounds
Dispense the mixture to prepared                         Allow curing in accordance to the minimum curing time at room          surface with trowel                                               temperature before operation

 

SEALXPERT PS108 HI-TEMP REPAIR PUTTY

 

Repair Putty for High Temperature | SEALXPERT PS108 HI-TEMP REPAIR PUTTY 

PACKAGE:

  • 454 gram/set